SYSTEM TI 5-BLANK is a non-precious dental milling alloy on Ti6Al4V, grade 5.
SYSTEM TI5-BLANK is intended for the use of crowns, bridges and implant supported structures.
SYSTEM TI5-BLANK has a proofed biocompatibility according DIN EN ISO 10993 with a good corrosion resistance.
Typical material properties
Yield strength 0,2 % (MPa) | 816 |
Elongation (%) | 8 |
Tensile strength (MPa) | 885 |
E-module (GPa) | 174 |
Density (g/cm³) | 4,4 |
Corrosion resistance (µg/cm²) | < 200 |
CTE (25 – 500°C) (10⁻⁶ K⁻¹) | 10,3 |
Hardness HV 10/30 | 318 |
Max. firing temperature (°C) | max. 800 |
Delivery form (mm) (X) = 8/10/12/14/15/16/18/20/25/27 | Ø 98,5 x (X) Ø 99,5 x (X) |
Applied Norms | DIN EN ISO 22674:2016 ASTM F 136 (z.T.) / DIN EN ISO 5832-3:2012 (z.T.) |
Lot numbers may show minimum deviation from typical values.
More information are available on our instruction for use.
Typical composition %
Ti | Al | V | O | Fe | C | N | H |
Bal. | 5,5 – 6,5 | 3,5 – 4,5 | 0,13 | 0,25 | 0,08 | 0,05 | 0,012 |